Some time ago I posted about my attempt to create a business style Poken out of Fimo. Well, this is the result:

As you can see I did a very rough polishing job. The problem was that the form was heated too long (or too hot) and got pretty fragile. Even while filing it a little, [...]

As announced in the last post: Fimo, baby! If you don’t know Fimo, it’s a lot like modeling clay, but you can harden it in your oven. After hardening, it’s like a long lasting, very hard rubber that can be filed, sawed etc. So it’s a great material to create casings of any kind.
In this [...]